Resin (IIR)
Calcined product, vinyl functionalized.
Aktifit VM is applicable specially for resin crosslinking of butyl-rubber (IIR).
The product as counter product to surface-treated calcined kaolinite offers improved processing and aging properties as well as better compression set.
- very low sieve residue
- very low chloride content
- long flow time with short vulcanization time
- high tensile modulus
- low compression set
- good hot air aging properties
- sealing tightness at high soldering temperatures
| Product characteristics | Unit | Testing method | AKTIFIT VM |
|---|---|---|---|
| Functionalization | vinyl | ||
|
Color values L*
Color values a*
Color values b*
|
acc. to CIELAB |
96.3
- 0.1
1.0
|
|
|
Particle size D50
Particle size D97
|
µm | acc. to ISO 13320-1 |
2.0
10.0
|
|
Residue > 40 µm
|
mg/kg | acc. to DIN EN ISO 787 part 18 |
10
|
| Volatile matter at 105 °C | % | acc. to DIN EN ISO 787 part 2 | 0.1 |
| pH Value | acc. to DIN EN ISO 787 part 9 | not applicable | |
|
Density
Bulk density
Tamped density
|
g/cm³ |
acc. to DIN EN ISO 787 part 10
acc. to DIN ISO 903-1976
acc. to DIN EN ISO 787 part 11
|
2.6
0.37
0.67
|
|
Spec. Surface area (BET)
Oil absorption
|
m²/g
g/100 g
|
acc. to DIN ISO 9277
acc. to DIN EN ISO 787 part 5
|
9
65
|
|
Hardness silica/kaolinite
|
mg |
acc. to Mohs
|
7/4.5
|
| Refractive index n | sin α / sin β | 1.55 | |
|
Water solubility
Acid solubility
|
% |
acc. to DIN EN ISO 787 part 3
acc. to DIN 53770 (0,1 N HCL)
|
not applicable
not applicable
|
|
Chemical Analysis:
SiO2
Al2O3
Fe2O3
|
% | acc. to DIN 51001 (RFA) |
86
13
< 1
|
|
Mineralogical Composition:
Neuburg silica
Calcined kaolinite
|
% | Based on X-ray diffraction pattern analysis combined with Rietveld |
60
40
|
|
Equilibrium moisture content at 25°C
and 50% relative humidity
and 80% relative humidity
and 90% relative humidity
|
% | acc. to DIN 66138 |
0.05
0.07
0.08
|
| Water absorption | ml/g | acc. to Baumann | 0.1 |
| hydrophobic | X | ||
| reactive | X |
resin cure
- High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/8) (M 620.0/19)
- Medium mineral filler / carbon black loading; 70/75 Shore A; IIR; resin cure (M 620.1/8)
- High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/20) (M 620.0/17)
In order to make available to you the most important information about our products at all times, you will find here the Material Specification.
The aspects to observe when working with our products are detailed in our Material Safety Data Sheet, which also can be downloaded.
All information about material characteristics, application fields and benefits can be found in this Technical Data Sheet and is also for download available here.
More recommended Products
Sorted by crosslinking agent.