Other applications
FKM compounds
Advantages
- very low sieve residue
- good mixing and dispersion properties
- high tensile strength
- high abrasion resistance
- long flow time with short vulcanization time
- easy deflashing
- low compression set
- good resistance against fuel, oil, water, acid
- avoidance of mold fouling caused by filler
Recommended Products
Specially for peroxide crosslinking | Sillitin Z 86 | Sillitin V 88 | Aktisil AM | Aktisil VM 56 | Aktisil Q |
|---|---|---|---|---|---|
| Plating/Mold fouling | |||||
| Viscosity | |||||
| Cure rate | |||||
| Tensile strength | |||||
| Elongation at break | |||||
| Moduli | |||||
| Tear resistance | |||||
| Compression set | 1) | ||||
| Compression set acc. to VW | |||||
| Abrasion resistance | |||||
| Heat resistance | 2) | ||||
| Resistance to acetic acid | |||||
| Fuel resistance | |||||
| Oil resistance | |||||
| To product | To product | To product | To product | To product |
1) no post-cure
2) positive change of tensile strength and elongation at break
low
high
Optimum
Specially for bisphenol crosslinking | Sillitin V 85 | Aktisil Q | Aktisil AM |
|---|---|---|---|
| Plating/Mold fouling | no | ||
| Tensile strength | |||
| Elongation at break | |||
| Moduli | |||
| Tear resistance | |||
| Compression set | |||
| Abrasion resistance | |||
| Heat resistance | |||
| Water resistance | |||
| Fuel resistance | |||
| Oil resistance | |||
| To product | To product | To product |
low
high
Optimum
Documents
Document | Download |
|---|---|
| Technical Data Sheet | |
| TDS Elastomers - Sillitin V 85 | |
| TDS Elastomers - Sillitin Z 86 / Z 86 puriss | |
| TDS Elastomers - Sillitin V 88 | |
| TDS Elastomers - Aktisil Q | |
| TDS Elastomers - Aktisil AM | |
| TDS Elastomers - Aktisil VM 56 | |
| Technical Poster | |
| Gloxil light iM16k MAM in peroxide cured FKM | |
| Technical Report | |
| Neuburg Siliceous Earth in bisphenolic cured FKM vs. N990 | |
| Neuburg Siliceous Earth in bisphenolic cured FKM vs. wollastonite and barium sulfate | |
| Neuburg Siliceous Earth in peroxide cured FKM vs. N990 | |
| Neuburg Siliceous Earth in peroxide cured FKM vs. wollastonite and barium sulfate | |
| Gloxil light iM16k MAM - Functionalized hollow glass microspheres in peroxide cured FKM | |
Guide Formulations
| 70 Shore A; FKM; bisphenol cure (RRS 39) | |
| 70 Shore A; FKM; bisphenol cure (RRS 40) | |
| 70 Shore A; FKM; bisphenol cure (RRS 41) | |
| 70 Shore A; FKM; bisphenol cure (RRS 42) | |
| 70 Shore A; FKM; bisphenol cure (RRS 43) | |
| Low viscosity, high curative level; 80 Shore A; FKM; bisphenol cure (M 629.3/2) | |
| Low viscosity, high curative level; 80 Shore A; FKM; bisphenol cure (M 629.3/6) | |
| Low viscosity, high curative level; 80 Shore A; FKM; bisphenol cure (M 629.1/2) | |