Automotive
Molded gaskets, o-rings and radial shaft seals
Advantages
- very low sieve residue
- good mixing and dispersion properties
- long flow time with short vulcanization time
- easy deflashing
- low compression set
- good resistance against fuel, oil, water, acid
- avoidance of mold fouling caused by filler
Recommended Products
Sillitin N 75 | Sillitin N 85 | Sillitin Z 86 | Sillitin P 87 | Silfit Z 911) | |
|---|---|---|---|---|---|
| Dispersibility | |||||
| Wear | |||||
| Plating/Mold fouling | no | ||||
| Brightness | |||||
| Color neutrality | |||||
| Tensile strength | |||||
| Tear resistance | |||||
| Compression set | |||||
| To product | To product | To product | To product | To product |
1) less moisture than Sillitin; very fine cell structure in sponge rubber
low
high
Optimum
Specially for sulphur and metaloxide crosslinking | Aktisil PF 216 | Aktisil AM | Aktifit AM1) |
|---|---|---|---|
| Cure rate | |||
| Tensile strength | |||
| Moduli | |||
| Compression set | |||
| Abrasion resistance | |||
| Chemical resistance | |||
| To product | To product | To product |
1) less moisture than Aktisil
low
high
Optimum
Specially for diamine crosslinking (ACM, AEM) | Aktisil Q |
|---|---|
| Tensile strength | |
| Moduli | |
| Compression set | |
| Abrasion resistance | |
| Chemical resistance | |
| To product |
Specially for peroxide crosslinking | Aktisil VM 56 | Aktisil VM 56/89 | Aktisil Q1) | Aktifit VM2) | Aktifit Q2) |
|---|---|---|---|---|---|
| Dispersibility | |||||
| Color neutrality | |||||
| Tensile strength | |||||
| Moduli | |||||
| Compression set | |||||
| Abrasion resistance | |||||
| Chemical resistance | |||||
| To product | To product | To product | To product | To product |
1) lower viscosity; best product for silicone rubber
2) less moisture
low
high
Optimum
Documents
Document | Download |
|---|---|
| Technical Data Sheet | |
| TDS Elastomers - Sillitin N 75 | |
| TDS Elastomers - Sillitin N 85 / N 85 puriss | |
| TDS Elastomers - Sillitin Z 86 / Z 86 puriss | |
| TDS Elastomers - Sillitin P 87 / P 87 puriss | |
| TDS Elastomers - Silfit Z 91 | |
| TDS Elastomers - Aktisil PF 216 | |
| TDS Elastomers - Aktifit AM | |
| TDS Elastomers - Aktisil VM 56 | |
| TDS Elastomers - Aktisil VM 56/89 | |
| TDS Elastomers - Aktisil Q | |
| TDS Elastomers - Aktifit VM | |
| TDS Elastomers - Aktifit Q | |
| Technical Poster | |
| Molded NBR parts for automotive oil seals ASTM 2000 - Replacement of carbon black N 990 | |
| Technical Report | |
| Aktisil Q in AEM seals and gaskets | |
| Molded NBR Parts for automotive oil seals ASTM D2000 - Replacement of carbon black N990 | |
Guide Formulations
| Quarter light gasket, nitrosamine reducing; 65 Shore A; EPDM; sulfur cure, injection molding (K 91-59) | |
| Quarter light gasket, Renault 2 6 07 B1; 60 Shore A; EPDM; sulfur cure, injection / transfer molding (911 C 152) | |
| Corner molding for sponge seals; 30 Shore A; EPDM; sulfur cure (A.1.4.002) | |
| Quarter light gasket; 50 Shore A; EPDM; sulfur cure (A.4.0.003) | |
| Parts with moderate resistance to lubricants and fuel, thermally stressable 100-130°C; 70 Shore A; CR; injection / transfer molding (T.I.B. 4.1.2) | |
| Rear light gasket, Bosch VS 15441; 25 Shore A; PNR; sulfur cure, injection molding (RRS 12) | |
| Silencer mounting; 55 Shore A; NR; sulfur cure (RRS 15) | |
| Resistant to Diesel and rape-oil methyl ester (RME); 65 Shore A; HNBR; peroxide cure (RRS 36) | |
| Gasket and O-Ring, Aktisil Q versus carbon black N-550, according to PSA S22 5106; 60 Shore A; AEM; diamine cure (M 621.7/1) | |
| Gasket and O-Ring, Aktisil Q versus carbon black N-550, according to PSA S22 5106; 60 Shore A; AEM; diamine cure (M 621.8/8) | |
| Gasket and O-Ring, Aktisil Q versus carbon black N-550, according to PSA S22 5106; 60 Shore A; AEM; diamine cure (M 621.8/9) | |
| Gasket and O-Ring, Aktifit AM in combination with silica in AEM; 70/80 Shore A; AEM, diamine cure (AEM 9913) | |
| Gasket and O-Ring, Aktifit AM in combination with silica in AEM; 70/80 Shore A; AEM, diamine cure (AEM 9914) | |
| Gasket and O-Ring, Aktifit AM in combination with silica in AEM; 70/80 Shore A; AEM, diamine cure (AEM 9919) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/1) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/7) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/3) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/2) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/5) | |
| Molded parts for automotive seals, ASTM D2000, replacement of carbon black N-990; 70 Shore A; NBR; sulfur cure (M 630.0/6) | |