Cable and electrical industry
Capacitor gaskets
Advantages
- very low sieve residue
- very low chloride content
- long flow time with short vulcanization time
- high tensile modulus
- low compression set
- good hot air aging properties
- sealing tightness at high soldering temperatures
- avoidance of mold fouling caused by filler
Recommended Products
Guide Formulations
| 70 Shore A; IIR; sulfur cure (M 231.0/1) | |
| Medium mineral filler / carbon black loading; 70/75 Shore A; IIR; resin cure (M 620.1/3) | |
| Medium mineral filler / carbon black loading; 70/75 Shore A; IIR; resin cure (M 620.1/4) | |
| Medium mineral filler / carbon black loading; 70/75 Shore A; IIR; resin cure (M 620.1/8) | |
| High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/3) | |
| High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/4) | |
| High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/8) | |
| High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/19) | |
| High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/12) | |
| High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/13) | |
| High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/17) | |
| High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/20) | |