Cable and electrical industry
Cable sheaths, cable insulation
Advantages
- very good extrusion properties
- medium to high tensile strength
- good compressive properties at high temperature
- good hot set properties
- high electrical resistivity, also after immersion in water
- avoidance of deposits on dies caused by filler
- good resistance against oil, water, acid
- very low dielectric loss, also after immersion in water, even without additional silane in the compound
Recommended Products
Sillitin Z 86 | Silfit Z 911) | |
|---|---|---|
| Dispersibility | ||
| Plating/Mold fouling | no | |
| Brightness | ||
| Color neutrality | ||
| Compression set | ||
| Dielectric loss | ||
| To product | To product |
1) less moisture than Sillitin
low
high
Optimum
Specially for sulphur and metaloxide crosslinking | Aktisil PF 216 | Aktisil AM | Aktifit AM1) |
|---|---|---|---|
| Dispersibility | |||
| Plating/Mold fouling | no | ||
| Cure rate | |||
| Tensile strength | |||
| Moduli | |||
| Compression set | |||
| Abrasion resistance | |||
| Chemical resistance | |||
| To product | To product | To product |
1) less moisture than Aktisil
low
high
Optimum
Specially for peroxide crosslinking | Aktisil VM 56 | Aktisil VM 56/89 | Aktisil Q1) | Aktifit VM2) |
|---|---|---|---|---|
| Dispersibility | ||||
| Plating/Mold fouling | no | |||
| Color neutrality | ||||
| Tensile strength | ||||
| Moduli | ||||
| Compression set | ||||
| Abrasion resistance | ||||
| Chemical resistance | ||||
| Electrical resistivity after exposure to water | ||||
| Dielectric loss | ||||
| Dielectric loss3) | ||||
| To product | To product | To product | To product |
1) lower viscosity; best product for silicone rubber
2) less moisture than Aktisil; even after storage in water; even without additional silane
3) even after storage in water; even without additional silane
low
high
Optimum
Documents
Document | Download |
|---|---|
| Technical Data Sheet | |
| TDS Elastomers - Sillitin Z 86 / Z 86 puriss | |
| TDS Elastomers - Silfit Z 91 | |
| TDS Elastomers - Aktisil PF 216 | |
| TDS Elastomers - Aktifit AM | |
| TDS Elastomers - Aktisil VM 56 | |
| TDS Elastomers - Aktisil VM 56/89 | |
| TDS Elastomers - Aktisil Q | |
| TDS Elastomers - Aktifit VM | |
| Technical Poster | |
| Calcined Neuburg Siliceous Earth in high voltage insulations | |
| Non-black fillers in peroxide cured EPDM cable insulation compounds | |
| Technical Report | |
| Non-black fillers in peroxide cured EPDM cable insulation compounds | |
| Calcined Neuburg Siliceous Earth in medium and high voltage cable insulations | |
Guide Formulations
| 70 Shore A; EPDM; peroxide cure (M 432.0/3) | |
| 70 Shore A; EPDM; peroxide cure (M 432.0/4) | |
| 70 Shore A; EPDM; peroxide cure (M 432.0/8) | |
| 70 Shore A; EPDM; peroxide cure (M 432.0/9) | |
| Medium and high voltage cable insulation; 85 Shore A; EPDM; peroxide cure (M 613.1/6) | |
| Medium and high voltage cable insulation; 85 Shore A; EPDM; peroxide cure (M 613.1/9) | |
| Medium and high voltage cable insulation; 85 Shore A; EPDM; peroxide cure (M 613.1/15) | |
| Light-colored; 50 Shore A; EPDM; sulfur cure (RRS 29) | |
| High tensile strength; 60 Shore A; peroxide cure (K 1322) | |
| 60 Shore A; EPDM; peroxide cure (3386 K460) | |
| DIN VDE 0207 3GM2; 75 Shore A; EPDM; peroxide cure (E.1.0.003) | |
| DIN VDE 0207 EM1; 75 Shore A; EPDM; peroxide cure (E.1.0.004) | |
| DIN VDE 0207 EM1; 55 Shore A; EPDM; sulfur cure (E.1.0.005) | |
| DIN VDE 0207 EM1; 70 Shore A; EPDM; sulfur cure (E.1.0.006) | |
| Semko; 65 Shore A; EPDM; peroxide cure (E.1.0.001) | |